Cyg Tefa Co., Ltd.
Professional Crosslinked PE Foam Manufacturer e-mail : cyg@cytefa.com
Add to Cart
Polyethylene Foam 25-30mm Marine Chemically Cross Linked Foam Raw Material
Polyethylene foam sheets xlpe foam is made of Low-Density PE Polymer. Commonly made and used as an insulation & protective material for various Industry applications.CYG foam is a strong, resilient closed-cell foam and it has several outstanding physical properties such as;
| ||||
| Property | Standard | Unit | Value | |
| Density | - | Kg/m³ | 33.33 | |
| Tensile Strength | Transverse | ISO-1798 | MPa | 0.39~0.41 |
| Longitudinal | 0.23~0.28 | |||
| Tearing Strength | Transverse | ISO-8067
| Kn/m | 1.84~2.26 |
| Longitudinal | 1.32~1.40 | |||
| Compression 25% | ISO-3386-1 | kPa | 36.80 | |
| Compression 45% | ISO-3386-1 | kPa | 66.70 | |
| Compression 50% | ISO-3386-1 | kPa | 96.90 | |
| Compression Set 25% 0.5H | ISO-1856 | % | 15.80 | |
| Compression Set 25% 24H | ISO-1856 | % | 5.80 | |
| Operating Temperature Range | Internal | °C | (-40,+80) | |
| Water Absorption % Volume (Maximum) | Internal | % | 0.50 | |
| Thermal Conductivity | JIS A1412-2 | W/mK | 0.040 | |
| Shore - C | ASTM D2240 | °C | 23 | |
| Flammability | FMVSS302 | mm/min | - | |
Additional Information
● All tests were carried out in 23°C ± 2.
● Data represents typical values measured on a 15mm thick specimen and should be considered as guidelines only.
● Processing method by eletronic heating.
● 12 kg/100m2 glue.
Advantages
1. Light weight, good elasticity
2. Weatherproof and waterproof
3. Flame retardant
4. Sound absorption
5. Heat insulation
6. Thermal insulation
7. Elastic and flexibility
8. Shock absorption
Applications